We offer Whytheat K 60% Alumina Dense Castable, which has an alumina content of 60% can be used for service temperatures upto 1600ºC. This castable also has a low iron content and can resist carbon monoxide attack. It can be used in various industries like: blast furnaces, foundries, boiler industry stoker arches, soak pit covers, forge furnaces, tunnel kilns, heat treatment furnace car tops as well as electro - phosphorus furnaces.
| Product Type | Whytheat K |
|---|---|
| Nature Of Bond | Hydraulic |
| Installation | Vibrations Casting |
| General Properties | |
| Max.Service Temperature | 1600. c |
| Maximum Grain Size | 5mm |
| Water Required For Casting | 10.6-11.8 |
| Chemical Analysis % | Typical Value |
| AI2o3 | 56 - 60 |
| Fe2o3 | 1.00 - 1.25 |
| Cao | 4.00 - 4.70 |
| Physical Properties | |
| Bulk Density | g/cc |
| Afer Drying At 110c/24 Hrs | 2.15 - 2.25 |
| CCS, kg/cm2 After Drying AT 110.C/24hrs | 350 - 430 |
| After Heating At 1100. C/3 hrs | 180 - 280 |
| After Heating At 1550. C/3 hrs | 350 - 500 |
| % Retained On max. Size | 0 - 5 |
| Thermal Properties | |
| Refractoriness, Orton / .C | 0.018419489 |
| PLC% | |
| after heating at 1100.C/3 hrs | -0.40 to + 0.20 |
| after heating at 1550.C/3 hrs | -1.20 to 2.40 |
| packaging | 25 kg bags |
| storage life | 6 months |
| delivery state | dry |